This thesis is focused the structural and spectroscopic characterization of multiferroic heterostructures composed of a thin film of iron, which is ferromagnetic, deposited on a bulk PMN-PT ([Pb(Mg1/3Nb2/3)O3]1−x–[PbTiO3]x) substrate, which is ferroelectric. The epitaxially grown interface between two mate-rials displays the magnetoelectric coupling. By applying an electric field across the thickness of the substrate (i.e. along the growth direction) it is possible to polarize and deform the ferroelectric crystal structure, thus manipulating the magnetic properties of the over-layer. In this work, we analyse how the two opposite polarized states of the PMN-PT affect the magnetic anisotropy of the iron overlayer and the role of morphology in this modifications. In particular the morphology represents an important factor in the magnetoelectric mechanisms that has been little investigated before.
NFFA Thesis
University of Milan PhD Thesis, (2019)
Strain-mediated magneto electric coupling and beyond: case studies by in-operando spectroscopy
I explored the properties of systems that were fabricated aiming to exploit enhanced multiferroic behavior and potentially useful functionalities at room temperature. The systems of choice for this thesis were two prototypical multiferroic heterostructures composed by a ferromagnetic thin film deposited on a ferroelectric substrate: LSMO/BTO(001) and Fe,FeMn/PMN-PT(001). I focused on the magnetic response of the thin films to applied electric fields oriented perpendicular to the interface, and influencing the substrate. In both the chosen heterostructures the magnetic layers and ferroelectric substrates are all materials with high ordering temperature.
In this work, I am going to present the main results of the scientific activity in which I was involved during my summer internship at CNR-IOM in Trieste (Italy) during the period, May 16, 2019 to August 10, 2019.
This report focuses on the magneto-optic Kerr effect (MOKE) investigations done on two set of samples. The first set of samples regards the optimization of the deposition parameters of CoFeB, in order to obtain a sample with low coercive field and isotropic behavior. The aim is to obtain a soft isotropic ferromagnetic layer, for further implementation into ferroelectric/ferromagnetic heterostructures. The second set regards a run of experiments with the aim of setting an exchange bias coupling by partially oxidizing the ferromagnetic layer through the substrate deoxidation. Here Fe (10 nm) ferromagnetic layer is deposited on substrate Lithium Niobate (LNZ).
NFFA Thesis
University of Milan Bachelor's Degree Thesis, (2019)
All-resolved photoemission spectroscopy of Fe(100) and passivated Fe-p(1x1)O surfaces
A.M. Finardi (Supervisors: G. Rossi, I. Vobornik, J. Fujii)
Le proprietà ottiche, elettroniche e magnetiche dei solidi e delle loro superfici dipendono dalla struttura degli stati elettronici entro alcuni eV dal livello di Fermi. I calcoli della struttura elettronica a bande sono efficaci solo nel caso di materiali a bassa interazione elettrone-elettrone (correlazione). L'esperimento e la guida necessaria per lo studio delle proprietà elettroniche dei solidi e delle loro superfici, ed in particolare la spettroscopia di fotoemissione (photoemission spectroscopy - PES) che si basa sulla misura dello spettro energetico degli elettroni emessi da un solido eccitato da un fascio di fotoni monocromatici di energia eccedente la funzione lavoro. La risoluzione dell'angolo di emissione (Angle-resolved photemission spectroscopy - ARPES) permette di avere informazioni sulla legge di dispersione En(k) dello stato elettronico iniziale, mentre la misura del grado di polarizzazione in spin del fascio di elettroni completa il set di numeri quantici, fornendo un dato molto importante per lo studio delle correlazioni elettroniche.